AISI 317LM Stainless Steel vs. C44500 Brass

AISI 317LM stainless steel belongs to the iron alloys classification, while C44500 brass belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AISI 317LM stainless steel and the bottom bar is C44500 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 79
41
Tensile Strength: Ultimate (UTS), MPa 590
350
Tensile Strength: Yield (Proof), MPa 230
120

Thermal Properties

Latent Heat of Fusion, J/g 300
180
Maximum Temperature: Mechanical, °C 300
140
Melting Completion (Liquidus), °C 1460
940
Melting Onset (Solidus), °C 1410
900
Specific Heat Capacity, J/kg-K 470
380
Thermal Conductivity, W/m-K 14
110
Thermal Expansion, µm/m-K 16
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
25
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
27

Otherwise Unclassified Properties

Base Metal Price, % relative 24
26
Density, g/cm3 8.0
8.3
Embodied Carbon, kg CO2/kg material 4.8
2.7
Embodied Energy, MJ/kg 65
46
Embodied Water, L/kg 170
330

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 130
65
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 21
12
Strength to Weight: Bending, points 20
13
Thermal Diffusivity, mm2/s 3.8
35
Thermal Shock Resistance, points 13
12

Alloy Composition

Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 18 to 20
0
Copper (Cu), % 0
70 to 73
Iron (Fe), % 54.4 to 64.5
0 to 0.060
Lead (Pb), % 0
0 to 0.070
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 13.5 to 17.5
0
Nitrogen (N), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.045
0.020 to 0.1
Silicon (Si), % 0 to 0.75
0
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0.9 to 1.2
Zinc (Zn), % 0
25.2 to 29.1
Residuals, % 0
0 to 0.4