AISI 317LMN Stainless Steel vs. EN 1.3539 Steel

Both AISI 317LMN stainless steel and EN 1.3539 steel are iron alloys. They have 64% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AISI 317LMN stainless steel and the bottom bar is EN 1.3539 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 620
670

Thermal Properties

Latent Heat of Fusion, J/g 290
260
Maximum Temperature: Mechanical, °C 1020
450
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
39
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 24
3.2
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 4.8
1.7
Embodied Energy, MJ/kg 65
22
Embodied Water, L/kg 170
57

Common Calculations

PREN (Pitting Resistance) 36
3.8
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
24
Strength to Weight: Bending, points 20
22
Thermal Diffusivity, mm2/s 3.8
11
Thermal Shock Resistance, points 14
20

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.030
0.93 to 1.1
Chromium (Cr), % 17 to 20
1.8 to 2.1
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 54.4 to 65.4
95.2 to 96.5
Manganese (Mn), % 0 to 2.0
0.8 to 1.1
Molybdenum (Mo), % 4.0 to 5.0
0.5 to 0.6
Nickel (Ni), % 13.5 to 17.5
0
Nitrogen (N), % 0.1 to 0.2
0
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 0.75
0.4 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.030