AISI 317LMN Stainless Steel vs. EN 1.8153 Steel

Both AISI 317LMN stainless steel and EN 1.8153 steel are iron alloys. They have 61% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AISI 317LMN stainless steel and the bottom bar is EN 1.8153 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
200 to 570
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
72
Tensile Strength: Ultimate (UTS), MPa 620
670 to 2040

Thermal Properties

Latent Heat of Fusion, J/g 290
270
Maximum Temperature: Mechanical, °C 1020
410
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1410
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 14
45
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 24
2.1
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 4.8
1.8
Embodied Energy, MJ/kg 65
25
Embodied Water, L/kg 170
48

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
24 to 74
Strength to Weight: Bending, points 20
22 to 46
Thermal Diffusivity, mm2/s 3.8
12
Thermal Shock Resistance, points 14
20 to 62

Alloy Composition

Carbon (C), % 0 to 0.030
0.56 to 0.64
Chromium (Cr), % 17 to 20
0.2 to 0.4
Iron (Fe), % 54.4 to 65.4
95.7 to 96.9
Manganese (Mn), % 0 to 2.0
0.7 to 1.0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 13.5 to 17.5
0
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 0.75
1.5 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.025
Vanadium (V), % 0
0.1 to 0.2