AISI 317LMN Stainless Steel vs. EN 2.4951 Nickel

AISI 317LMN stainless steel belongs to the iron alloys classification, while EN 2.4951 nickel belongs to the nickel alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 317LMN stainless steel and the bottom bar is EN 2.4951 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
34
Fatigue Strength, MPa 250
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
76
Shear Strength, MPa 430
500
Tensile Strength: Ultimate (UTS), MPa 620
750
Tensile Strength: Yield (Proof), MPa 270
270

Thermal Properties

Latent Heat of Fusion, J/g 290
320
Maximum Temperature: Mechanical, °C 1020
1150
Melting Completion (Liquidus), °C 1460
1360
Melting Onset (Solidus), °C 1410
1310
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 14
12
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
1.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
1.7

Otherwise Unclassified Properties

Base Metal Price, % relative 24
60
Density, g/cm3 8.0
8.5
Embodied Carbon, kg CO2/kg material 4.8
9.3
Embodied Energy, MJ/kg 65
130
Embodied Water, L/kg 170
280

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
200
Resilience: Unit (Modulus of Resilience), kJ/m3 180
190
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 22
25
Strength to Weight: Bending, points 20
22
Thermal Diffusivity, mm2/s 3.8
3.1
Thermal Shock Resistance, points 14
23

Alloy Composition

Aluminum (Al), % 0
0 to 0.3
Carbon (C), % 0 to 0.030
0.080 to 0.15
Chromium (Cr), % 17 to 20
18 to 21
Cobalt (Co), % 0
0 to 5.0
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 54.4 to 65.4
0 to 5.0
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 13.5 to 17.5
65.4 to 81.7
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.020
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0.2 to 0.6