AISI 321 Stainless Steel vs. Grade 365 Molybdenum
AISI 321 stainless steel belongs to the iron alloys classification, while grade 365 molybdenum belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is AISI 321 stainless steel and the bottom bar is grade 365 molybdenum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 310 |
| Elongation at Break, % | 34 to 50 | |
| 6.3 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 77 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 590 to 690 | |
| 620 |
| Tensile Strength: Yield (Proof), MPa | 220 to 350 | |
| 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 370 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 250 |
| Thermal Expansion, µm/m-K | 17 | |
| 7.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 10 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 28 |
| Embodied Energy, MJ/kg | 45 | |
| 330 |
| Embodied Water, L/kg | 140 | |
| 360 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 to 230 | |
| 37 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 310 | |
| 450 |
| Stiffness to Weight: Axial, points | 14 | |
| 17 |
| Stiffness to Weight: Bending, points | 25 | |
| 22 |
| Strength to Weight: Axial, points | 21 to 25 | |
| 17 |
| Strength to Weight: Bending, points | 20 to 22 | |
| 16 |
| Thermal Shock Resistance, points | 13 to 15 | |
| 21 |
Alloy Composition
| Carbon (C), % | 0 to 0.080 | |
| 0 to 0.010 |
| Chromium (Cr), % | 17 to 19 | |
| 0 |
| Iron (Fe), % | 65.3 to 74 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 99.9 to 100 |
| Nickel (Ni), % | 9.0 to 12 | |
| 0 to 0.0020 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0 to 0.0020 |
| Oxygen (O), % | 0 | |
| 0 to 0.0015 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 0.010 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Titanium (Ti), % | 0 to 0.7 | |
| 0 |