AISI 347 Stainless Steel vs. EN 2.4889 Nickel

AISI 347 stainless steel belongs to the iron alloys classification, while EN 2.4889 nickel belongs to the nickel alloys. They have 53% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 347 stainless steel and the bottom bar is EN 2.4889 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 210
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34 to 46
39
Fatigue Strength, MPa 220 to 270
210
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Shear Strength, MPa 430 to 460
490
Tensile Strength: Ultimate (UTS), MPa 610 to 690
720
Tensile Strength: Yield (Proof), MPa 240 to 350
270

Thermal Properties

Latent Heat of Fusion, J/g 290
350
Maximum Temperature: Mechanical, °C 870
1200
Melting Completion (Liquidus), °C 1430
1350
Melting Onset (Solidus), °C 1400
1300
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
13
Thermal Expansion, µm/m-K 17
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 19
42
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 3.6
6.9
Embodied Energy, MJ/kg 52
98
Embodied Water, L/kg 150
250

Common Calculations

PREN (Pitting Resistance) 18
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190 to 220
220
Resilience: Unit (Modulus of Resilience), kJ/m3 150 to 310
180
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22 to 25
25
Strength to Weight: Bending, points 20 to 22
22
Thermal Diffusivity, mm2/s 4.3
3.4
Thermal Shock Resistance, points 13 to 15
19

Alloy Composition

Carbon (C), % 0 to 0.080
0.050 to 0.12
Cerium (Ce), % 0
0.030 to 0.090
Chromium (Cr), % 17 to 19
26 to 29
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 64.1 to 74
21 to 25
Manganese (Mn), % 0 to 2.0
0 to 1.0
Nickel (Ni), % 9.0 to 13
45 to 50.4
Niobium (Nb), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.045
0 to 0.020
Silicon (Si), % 0 to 0.75
2.5 to 3.0
Sulfur (S), % 0 to 0.030
0 to 0.010