AISI 347 Stainless Steel vs. EN AC-48100 Aluminum
AISI 347 stainless steel belongs to the iron alloys classification, while EN AC-48100 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is AISI 347 stainless steel and the bottom bar is EN AC-48100 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 210 | |
| 100 to 140 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 76 |
| Elongation at Break, % | 34 to 46 | |
| 1.1 |
| Fatigue Strength, MPa | 220 to 270 | |
| 120 to 130 |
| Poisson's Ratio | 0.28 | |
| 0.33 |
| Shear Modulus, GPa | 77 | |
| 29 |
| Tensile Strength: Ultimate (UTS), MPa | 610 to 690 | |
| 240 to 330 |
| Tensile Strength: Yield (Proof), MPa | 240 to 350 | |
| 190 to 300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 640 |
| Maximum Temperature: Mechanical, °C | 870 | |
| 170 |
| Melting Completion (Liquidus), °C | 1430 | |
| 580 |
| Melting Onset (Solidus), °C | 1400 | |
| 470 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 880 |
| Thermal Conductivity, W/m-K | 16 | |
| 130 |
| Thermal Expansion, µm/m-K | 17 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 87 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 19 | |
| 11 |
| Density, g/cm3 | 7.8 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 7.3 |
| Embodied Energy, MJ/kg | 52 | |
| 130 |
| Embodied Water, L/kg | 150 | |
| 940 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 to 220 | |
| 2.3 to 3.6 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 150 to 310 | |
| 250 to 580 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 25 | |
| 51 |
| Strength to Weight: Axial, points | 22 to 25 | |
| 24 to 33 |
| Strength to Weight: Bending, points | 20 to 22 | |
| 31 to 38 |
| Thermal Diffusivity, mm2/s | 4.3 | |
| 55 |
| Thermal Shock Resistance, points | 13 to 15 | |
| 11 to 16 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 72.1 to 79.8 |
| Carbon (C), % | 0 to 0.080 | |
| 0 |
| Chromium (Cr), % | 17 to 19 | |
| 0 |
| Copper (Cu), % | 0 | |
| 4.0 to 5.0 |
| Iron (Fe), % | 64.1 to 74 | |
| 0 to 1.3 |
| Magnesium (Mg), % | 0 | |
| 0.25 to 0.65 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 9.0 to 13 | |
| 0 to 0.3 |
| Niobium (Nb), % | 0 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 0.75 | |
| 16 to 18 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.15 |
| Titanium (Ti), % | 0 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 | |
| 0 to 1.5 |
| Residuals, % | 0 | |
| 0 to 0.25 |