AISI 347 Stainless Steel vs. C67600 Bronze

AISI 347 stainless steel belongs to the iron alloys classification, while C67600 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 347 stainless steel and the bottom bar is C67600 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
100
Elongation at Break, % 34 to 46
13 to 33
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 77
40
Shear Strength, MPa 430 to 460
270 to 350
Tensile Strength: Ultimate (UTS), MPa 610 to 690
430 to 570
Tensile Strength: Yield (Proof), MPa 240 to 350
170 to 380

Thermal Properties

Latent Heat of Fusion, J/g 290
170
Maximum Temperature: Mechanical, °C 870
120
Melting Completion (Liquidus), °C 1430
890
Melting Onset (Solidus), °C 1400
870
Specific Heat Capacity, J/kg-K 480
380
Thermal Conductivity, W/m-K 16
110
Thermal Expansion, µm/m-K 17
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
24
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
27

Otherwise Unclassified Properties

Base Metal Price, % relative 19
23
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 3.6
2.8
Embodied Energy, MJ/kg 52
47
Embodied Water, L/kg 150
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190 to 220
63 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 150 to 310
140 to 680
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 22 to 25
15 to 20
Strength to Weight: Bending, points 20 to 22
16 to 19
Thermal Diffusivity, mm2/s 4.3
35
Thermal Shock Resistance, points 13 to 15
14 to 19

Alloy Composition

Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 17 to 19
0
Copper (Cu), % 0
57 to 60
Iron (Fe), % 64.1 to 74
0.4 to 1.3
Lead (Pb), % 0
0.5 to 1.0
Manganese (Mn), % 0 to 2.0
0.050 to 0.5
Nickel (Ni), % 9.0 to 13
0
Niobium (Nb), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 0.75
0
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0.5 to 1.5
Zinc (Zn), % 0
35.2 to 41.6
Residuals, % 0
0 to 0.5