AISI 347H Stainless Steel vs. C97600 Dairy Metal

AISI 347H stainless steel belongs to the iron alloys classification, while C97600 dairy metal belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AISI 347H stainless steel and the bottom bar is C97600 dairy metal.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 39
11
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 77
46
Tensile Strength: Ultimate (UTS), MPa 580
310
Tensile Strength: Yield (Proof), MPa 230
140

Thermal Properties

Latent Heat of Fusion, J/g 290
210
Maximum Temperature: Mechanical, °C 940
210
Melting Completion (Liquidus), °C 1430
1140
Melting Onset (Solidus), °C 1390
1110
Specific Heat Capacity, J/kg-K 480
380
Thermal Conductivity, W/m-K 16
22
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
5.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
5.1

Otherwise Unclassified Properties

Base Metal Price, % relative 19
37
Density, g/cm3 7.8
8.8
Embodied Carbon, kg CO2/kg material 3.6
4.6
Embodied Energy, MJ/kg 52
69
Embodied Water, L/kg 150
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
29
Resilience: Unit (Modulus of Resilience), kJ/m3 140
85
Stiffness to Weight: Axial, points 14
7.7
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 21
9.8
Strength to Weight: Bending, points 20
12
Thermal Diffusivity, mm2/s 4.2
6.5
Thermal Shock Resistance, points 13
11

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Carbon (C), % 0.040 to 0.1
0
Chromium (Cr), % 17 to 19
0
Copper (Cu), % 0
63 to 67
Iron (Fe), % 64.1 to 74
0 to 1.5
Lead (Pb), % 0
3.0 to 5.0
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 9.0 to 13
19 to 21.5
Niobium (Nb), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.045
0 to 0.050
Silicon (Si), % 0 to 0.75
0 to 0.15
Sulfur (S), % 0 to 0.030
0 to 0.080
Tin (Sn), % 0
3.5 to 4.0
Zinc (Zn), % 0
3.0 to 9.0
Residuals, % 0
0 to 0.3