AISI 403 Stainless Steel vs. EN 1.4371 Stainless Steel
Both AISI 403 stainless steel and EN 1.4371 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is AISI 403 stainless steel and the bottom bar is EN 1.4371 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 240 | |
| 220 to 230 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 16 to 25 | |
| 45 to 51 |
| Fatigue Strength, MPa | 200 to 340 | |
| 290 to 340 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 77 |
| Shear Strength, MPa | 340 to 480 | |
| 520 to 540 |
| Tensile Strength: Ultimate (UTS), MPa | 530 to 780 | |
| 740 to 750 |
| Tensile Strength: Yield (Proof), MPa | 280 to 570 | |
| 320 to 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 280 |
| Maximum Temperature: Corrosion, °C | 390 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 740 | |
| 880 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1410 |
| Melting Onset (Solidus), °C | 1400 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 28 | |
| 15 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 2.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 2.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 6.5 | |
| 12 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 2.6 |
| Embodied Energy, MJ/kg | 27 | |
| 38 |
| Embodied Water, L/kg | 99 | |
| 140 |
Common Calculations
| PREN (Pitting Resistance) | 12 | |
| 20 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 120 | |
| 270 to 310 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 840 | |
| 250 to 300 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 19 to 28 | |
| 27 |
| Strength to Weight: Bending, points | 19 to 24 | |
| 24 |
| Thermal Diffusivity, mm2/s | 7.6 | |
| 4.0 |
| Thermal Shock Resistance, points | 20 to 29 | |
| 16 |
Alloy Composition
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.030 |
| Chromium (Cr), % | 11.5 to 13 | |
| 16 to 17.5 |
| Copper (Cu), % | 0 | |
| 0 to 1.0 |
| Iron (Fe), % | 84.7 to 88.5 | |
| 66.7 to 74.4 |
| Manganese (Mn), % | 0 to 1.0 | |
| 6.0 to 8.0 |
| Nickel (Ni), % | 0 to 0.6 | |
| 3.5 to 5.5 |
| Nitrogen (N), % | 0 | |
| 0.15 to 0.25 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |