AISI 403 Stainless Steel vs. EN 1.4515 Stainless Steel

Both AISI 403 stainless steel and EN 1.4515 stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 403 stainless steel and the bottom bar is EN 1.4515 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 16 to 25
25
Fatigue Strength, MPa 200 to 340
380
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
80
Tensile Strength: Ultimate (UTS), MPa 530 to 780
730
Tensile Strength: Yield (Proof), MPa 280 to 570
550

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Maximum Temperature: Corrosion, °C 390
450
Maximum Temperature: Mechanical, °C 740
1100
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 28
16
Thermal Expansion, µm/m-K 9.9
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
19
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.9
3.8
Embodied Energy, MJ/kg 27
53
Embodied Water, L/kg 99
180

Common Calculations

PREN (Pitting Resistance) 12
38
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 120
170
Resilience: Unit (Modulus of Resilience), kJ/m3 210 to 840
730
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19 to 28
26
Strength to Weight: Bending, points 19 to 24
23
Thermal Diffusivity, mm2/s 7.6
4.3
Thermal Shock Resistance, points 20 to 29
20

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.030
Chromium (Cr), % 11.5 to 13
24.5 to 26.5
Copper (Cu), % 0
0.8 to 1.3
Iron (Fe), % 84.7 to 88.5
58.4 to 66.6
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0
2.5 to 3.5
Nickel (Ni), % 0 to 0.6
5.5 to 7.0
Nitrogen (N), % 0
0.12 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.020