AISI 403 Stainless Steel vs. N07041 Nickel
AISI 403 stainless steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is AISI 403 stainless steel and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Elongation at Break, % | 16 to 25 | |
| 14 |
| Fatigue Strength, MPa | 200 to 340 | |
| 540 |
| Shear Strength, MPa | 340 to 480 | |
| 850 |
| Tensile Strength: Ultimate (UTS), MPa | 530 to 780 | |
| 1400 |
| Tensile Strength: Yield (Proof), MPa | 280 to 570 | |
| 1050 |
Thermal Properties
| Melting Onset (Solidus), °C | 1400 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 450 |
| Thermal Conductivity, W/m-K | 28 | |
| 11 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 120 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 840 | |
| 2510 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 19 to 28 | |
| 47 |
| Strength to Weight: Bending, points | 19 to 24 | |
| 34 |
| Thermal Diffusivity, mm2/s | 7.6 | |
| 3.0 |
| Thermal Shock Resistance, points | 20 to 29 | |
| 38 |