AISI 405 Stainless Steel vs. EN 1.4308 Stainless Steel

Both AISI 405 stainless steel and EN 1.4308 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 405 stainless steel and the bottom bar is EN 1.4308 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
150
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
34
Fatigue Strength, MPa 130
160
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 470
510
Tensile Strength: Yield (Proof), MPa 200
200

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Maximum Temperature: Corrosion, °C 390
420
Maximum Temperature: Mechanical, °C 820
960
Melting Completion (Liquidus), °C 1530
1420
Melting Onset (Solidus), °C 1480
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 30
15
Thermal Expansion, µm/m-K 11
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
15
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.0
3.0
Embodied Energy, MJ/kg 28
43
Embodied Water, L/kg 100
150

Common Calculations

PREN (Pitting Resistance) 13
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 84
140
Resilience: Unit (Modulus of Resilience), kJ/m3 100
100
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
18
Strength to Weight: Bending, points 17
18
Thermal Diffusivity, mm2/s 8.1
4.1
Thermal Shock Resistance, points 16
11

Alloy Composition

Aluminum (Al), % 0.1 to 0.3
0
Carbon (C), % 0 to 0.080
0 to 0.070
Chromium (Cr), % 11.5 to 14.5
18 to 20
Iron (Fe), % 82.5 to 88.4
65.9 to 74
Manganese (Mn), % 0 to 1.0
0 to 1.5
Nickel (Ni), % 0 to 0.6
8.0 to 11
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.030