AISI 409Cb Stainless Steel vs. EV31A Magnesium

AISI 409Cb stainless steel belongs to the iron alloys classification, while EV31A magnesium belongs to the magnesium alloys. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AISI 409Cb stainless steel and the bottom bar is EV31A magnesium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
44
Elongation at Break, % 24
3.5
Fatigue Strength, MPa 140
120
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 75
17
Shear Strength, MPa 270
170
Tensile Strength: Ultimate (UTS), MPa 420
260
Tensile Strength: Yield (Proof), MPa 200
170

Thermal Properties

Maximum Temperature: Mechanical, °C 710
200
Melting Onset (Solidus), °C 1410
590
Specific Heat Capacity, J/kg-K 480
1000
Thermal Conductivity, W/m-K 25
86
Thermal Expansion, µm/m-K 10
27

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
18
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
90

Otherwise Unclassified Properties

Density, g/cm3 7.8
1.8

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83
8.1
Resilience: Unit (Modulus of Resilience), kJ/m3 100
330
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
65
Strength to Weight: Axial, points 15
40
Strength to Weight: Bending, points 16
50
Thermal Diffusivity, mm2/s 6.7
47
Thermal Shock Resistance, points 15
16