AISI 410 Stainless Steel vs. AWS E316L

Both AISI 410 stainless steel and AWS E316L are iron alloys. They have 78% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AISI 410 stainless steel and the bottom bar is AWS E316L.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 16 to 22
34
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
78
Tensile Strength: Ultimate (UTS), MPa 520 to 770
550

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Melting Completion (Liquidus), °C 1530
1440
Melting Onset (Solidus), °C 1480
1390
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 30
15
Thermal Expansion, µm/m-K 11
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
20
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 1.9
4.0
Embodied Energy, MJ/kg 27
55
Embodied Water, L/kg 100
160

Common Calculations

PREN (Pitting Resistance) 13
27
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19 to 28
19
Strength to Weight: Bending, points 19 to 24
19
Thermal Diffusivity, mm2/s 8.1
4.0
Thermal Shock Resistance, points 18 to 26
14

Alloy Composition

Carbon (C), % 0.080 to 0.15
0 to 0.040
Chromium (Cr), % 11.5 to 13.5
17 to 20
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 83.5 to 88.4
58.6 to 69.5
Manganese (Mn), % 0 to 1.0
0.5 to 2.5
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 0 to 0.75
11 to 14
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030