AISI 410 Stainless Steel vs. EN 1.4869 Casting Alloy
AISI 410 stainless steel belongs to the iron alloys classification, while EN 1.4869 casting alloy belongs to the nickel alloys. They have a modest 32% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is AISI 410 stainless steel and the bottom bar is EN 1.4869 casting alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 16 to 22 | |
| 5.7 |
| Fatigue Strength, MPa | 190 to 350 | |
| 130 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 770 | |
| 540 |
| Tensile Strength: Yield (Proof), MPa | 290 to 580 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 710 | |
| 1200 |
| Melting Completion (Liquidus), °C | 1530 | |
| 1450 |
| Melting Onset (Solidus), °C | 1480 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 460 |
| Thermal Conductivity, W/m-K | 30 | |
| 10 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.0 | |
| 70 |
| Density, g/cm3 | 7.7 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 7.7 |
| Embodied Energy, MJ/kg | 27 | |
| 110 |
| Embodied Water, L/kg | 100 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 97 to 110 | |
| 26 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 860 | |
| 230 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 19 to 28 | |
| 18 |
| Strength to Weight: Bending, points | 19 to 24 | |
| 17 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 2.6 |
| Thermal Shock Resistance, points | 18 to 26 | |
| 14 |
Alloy Composition
| Carbon (C), % | 0.080 to 0.15 | |
| 0.45 to 0.55 |
| Chromium (Cr), % | 11.5 to 13.5 | |
| 24 to 26 |
| Cobalt (Co), % | 0 | |
| 14 to 16 |
| Iron (Fe), % | 83.5 to 88.4 | |
| 11.4 to 23.6 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 to 0.75 | |
| 33 to 37 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 1.0 to 2.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 4.0 to 6.0 |