AISI 410 Stainless Steel vs. S42035 Stainless Steel
Both AISI 410 stainless steel and S42035 stainless steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is AISI 410 stainless steel and the bottom bar is S42035 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 240 | |
| 160 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 16 to 22 | |
| 18 |
| Fatigue Strength, MPa | 190 to 350 | |
| 260 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 77 |
| Shear Strength, MPa | 330 to 470 | |
| 390 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 770 | |
| 630 |
| Tensile Strength: Yield (Proof), MPa | 290 to 580 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 280 |
| Maximum Temperature: Corrosion, °C | 390 | |
| 470 |
| Maximum Temperature: Mechanical, °C | 710 | |
| 810 |
| Melting Completion (Liquidus), °C | 1530 | |
| 1450 |
| Melting Onset (Solidus), °C | 1480 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 30 | |
| 27 |
| Thermal Expansion, µm/m-K | 11 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 2.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 3.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.0 | |
| 9.5 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 2.4 |
| Embodied Energy, MJ/kg | 27 | |
| 34 |
| Embodied Water, L/kg | 100 | |
| 110 |
Common Calculations
| PREN (Pitting Resistance) | 13 | |
| 17 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 97 to 110 | |
| 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 860 | |
| 460 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 19 to 28 | |
| 22 |
| Strength to Weight: Bending, points | 19 to 24 | |
| 21 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 7.2 |
| Thermal Shock Resistance, points | 18 to 26 | |
| 22 |
Alloy Composition
| Carbon (C), % | 0.080 to 0.15 | |
| 0 to 0.080 |
| Chromium (Cr), % | 11.5 to 13.5 | |
| 13.5 to 15.5 |
| Iron (Fe), % | 83.5 to 88.4 | |
| 78.1 to 85 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0.2 to 1.2 |
| Nickel (Ni), % | 0 to 0.75 | |
| 1.0 to 2.5 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 | |
| 0.3 to 0.5 |