AISI 410Cb Stainless Steel vs. 90-silver 10-cadmium-oxide
AISI 410Cb stainless steel belongs to the iron alloys classification, while 90-silver 10-cadmium-oxide belongs to the otherwise unclassified metals. There are 8 material properties with values for both materials. Properties with values for just one material (26, in this case) are not shown.
For each property being compared, the top bar is AISI 410Cb stainless steel and the bottom bar is 90-silver 10-cadmium-oxide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.7 | |
| 10 |
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 72 to 100 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 64 to 91 |
| Elongation at Break, % | 15 | |
| 1.1 to 28 |
| Shear Strength, MPa | 340 to 590 | |
| 170 to 230 |
| Strength to Weight: Axial, points | 20 to 35 | |
| 7.0 to 11 |
| Strength to Weight: Bending, points | 19 to 28 | |
| 8.8 to 12 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 960 | |
| 260 to 400 |