AISI 410Cb Stainless Steel vs. EN 1.4539 Stainless Steel

Both AISI 410Cb stainless steel and EN 1.4539 stainless steel are iron alloys. They have 60% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 410Cb stainless steel and the bottom bar is EN 1.4539 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 270
200
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 15
38
Fatigue Strength, MPa 180 to 460
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
79
Shear Strength, MPa 340 to 590
430
Tensile Strength: Ultimate (UTS), MPa 550 to 960
630
Tensile Strength: Yield (Proof), MPa 310 to 790
260

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Maximum Temperature: Corrosion, °C 410
420
Maximum Temperature: Mechanical, °C 730
1100
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 27
12
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
31
Density, g/cm3 7.7
8.1
Embodied Carbon, kg CO2/kg material 2.0
5.7
Embodied Energy, MJ/kg 29
78
Embodied Water, L/kg 97
200

Common Calculations

PREN (Pitting Resistance) 12
36
Resilience: Ultimate (Unit Rupture Work), MJ/m3 70 to 130
190
Resilience: Unit (Modulus of Resilience), kJ/m3 240 to 1600
160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20 to 35
22
Strength to Weight: Bending, points 19 to 28
20
Thermal Diffusivity, mm2/s 7.3
3.2
Thermal Shock Resistance, points 20 to 35
14

Alloy Composition

Carbon (C), % 0 to 0.18
0 to 0.020
Chromium (Cr), % 11 to 13
19 to 21
Copper (Cu), % 0
1.2 to 2.0
Iron (Fe), % 84.5 to 89
43.1 to 51.8
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0
4.0 to 5.0
Nickel (Ni), % 0
24 to 26
Niobium (Nb), % 0.050 to 0.3
0
Nitrogen (N), % 0
0 to 0.15
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.7
Sulfur (S), % 0 to 0.030
0 to 0.010