AISI 410Cb Stainless Steel vs. N07041 Nickel
AISI 410Cb stainless steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is AISI 410Cb stainless steel and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Elongation at Break, % | 15 | |
| 14 |
| Fatigue Strength, MPa | 180 to 460 | |
| 540 |
| Shear Strength, MPa | 340 to 590 | |
| 850 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 960 | |
| 1400 |
| Tensile Strength: Yield (Proof), MPa | 310 to 790 | |
| 1050 |
Thermal Properties
| Melting Onset (Solidus), °C | 1400 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 450 |
| Thermal Conductivity, W/m-K | 27 | |
| 11 |
| Thermal Expansion, µm/m-K | 10 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.7 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 70 to 130 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 to 1600 | |
| 2510 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 20 to 35 | |
| 47 |
| Strength to Weight: Bending, points | 19 to 28 | |
| 34 |
| Thermal Diffusivity, mm2/s | 7.3 | |
| 3.0 |
| Thermal Shock Resistance, points | 20 to 35 | |
| 38 |