AISI 414 Stainless Steel vs. EN 1.4107 Stainless Steel
Both AISI 414 stainless steel and EN 1.4107 stainless steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is AISI 414 stainless steel and the bottom bar is EN 1.4107 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 17 | |
18 to 21 |
Fatigue Strength, MPa | 430 to 480 | |
260 to 350 |
Poisson's Ratio | 0.28 | |
0.28 |
Shear Modulus, GPa | 76 | |
76 |
Tensile Strength: Ultimate (UTS), MPa | 900 to 960 | |
620 to 700 |
Tensile Strength: Yield (Proof), MPa | 700 to 790 | |
400 to 570 |
Thermal Properties
Latent Heat of Fusion, J/g | 280 | |
270 |
Maximum Temperature: Corrosion, °C | 390 | |
390 |
Maximum Temperature: Mechanical, °C | 750 | |
740 |
Melting Completion (Liquidus), °C | 1440 | |
1450 |
Melting Onset (Solidus), °C | 1400 | |
1410 |
Specific Heat Capacity, J/kg-K | 480 | |
480 |
Thermal Conductivity, W/m-K | 25 | |
27 |
Thermal Expansion, µm/m-K | 10 | |
10 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.5 | |
2.9 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.9 | |
3.3 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 8.0 | |
7.5 |
Density, g/cm3 | 7.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 2.1 | |
2.1 |
Embodied Energy, MJ/kg | 29 | |
30 |
Embodied Water, L/kg | 100 | |
100 |
Common Calculations
PREN (Pitting Resistance) | 13 | |
13 |
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 150 | |
110 to 120 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 1260 to 1590 | |
420 to 840 |
Stiffness to Weight: Axial, points | 14 | |
14 |
Stiffness to Weight: Bending, points | 25 | |
25 |
Strength to Weight: Axial, points | 32 to 34 | |
22 to 25 |
Strength to Weight: Bending, points | 27 to 28 | |
21 to 22 |
Thermal Diffusivity, mm2/s | 6.7 | |
7.2 |
Thermal Shock Resistance, points | 33 to 35 | |
22 to 25 |
Alloy Composition
Carbon (C), % | 0 to 0.15 | |
0 to 0.1 |
Chromium (Cr), % | 11.5 to 13.5 | |
11.5 to 12.5 |
Copper (Cu), % | 0 | |
0 to 0.3 |
Iron (Fe), % | 81.8 to 87.3 | |
83.8 to 87.2 |
Manganese (Mn), % | 0 to 1.0 | |
0.5 to 0.8 |
Molybdenum (Mo), % | 0 | |
0 to 0.5 |
Nickel (Ni), % | 1.3 to 2.5 | |
0.8 to 1.5 |
Phosphorus (P), % | 0 to 0.040 | |
0 to 0.030 |
Silicon (Si), % | 0 to 1.0 | |
0 to 0.4 |
Sulfur (S), % | 0 to 0.030 | |
0 to 0.020 |
Vanadium (V), % | 0 | |
0 to 0.080 |