AISI 414 Stainless Steel vs. EN 1.5526 Steel

Both AISI 414 stainless steel and EN 1.5526 steel are iron alloys. They have 85% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AISI 414 stainless steel and the bottom bar is EN 1.5526 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Reduction in Area, % 50
65 to 71
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 900 to 960
490 to 1650

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 750
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
48
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 8.0
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.1
1.4
Embodied Energy, MJ/kg 29
19
Embodied Water, L/kg 100
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 32 to 34
17 to 59
Strength to Weight: Bending, points 27 to 28
18 to 40
Thermal Diffusivity, mm2/s 6.7
13
Thermal Shock Resistance, points 33 to 35
14 to 49

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.15
0.27 to 0.32
Chromium (Cr), % 11.5 to 13.5
0 to 0.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 81.8 to 87.3
97.7 to 98.9
Manganese (Mn), % 0 to 1.0
0.8 to 1.1
Nickel (Ni), % 1.3 to 2.5
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025