AISI 414 Stainless Steel vs. N07041 Nickel

AISI 414 stainless steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AISI 414 stainless steel and the bottom bar is N07041 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Elongation at Break, % 17
14
Fatigue Strength, MPa 430 to 480
540
Shear Strength, MPa 550 to 590
850
Tensile Strength: Ultimate (UTS), MPa 900 to 960
1400
Tensile Strength: Yield (Proof), MPa 700 to 790
1050

Thermal Properties

Melting Onset (Solidus), °C 1400
1320
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 25
11
Thermal Expansion, µm/m-K 10
12

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.2

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 150
180
Resilience: Unit (Modulus of Resilience), kJ/m3 1260 to 1590
2510
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 32 to 34
47
Strength to Weight: Bending, points 27 to 28
34
Thermal Diffusivity, mm2/s 6.7
3.0
Thermal Shock Resistance, points 33 to 35
38