AISI 415 Stainless Steel vs. R30816 Cobalt
AISI 415 stainless steel belongs to the iron alloys classification, while R30816 cobalt belongs to the cobalt alloys. They have a modest 22% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is AISI 415 stainless steel and the bottom bar is R30816 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 260 | |
| 280 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Elongation at Break, % | 17 | |
| 23 |
| Fatigue Strength, MPa | 430 | |
| 250 |
| Poisson's Ratio | 0.28 | |
| 0.3 |
| Reduction in Area, % | 50 | |
| 22 |
| Shear Modulus, GPa | 76 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 900 | |
| 1020 |
| Tensile Strength: Yield (Proof), MPa | 700 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 300 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1540 |
| Melting Onset (Solidus), °C | 1400 | |
| 1460 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 420 |
| Thermal Conductivity, W/m-K | 24 | |
| 13 |
| Thermal Expansion, µm/m-K | 10 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 9.1 |
| Embodied Carbon, kg CO2/kg material | 2.5 | |
| 20 |
| Embodied Energy, MJ/kg | 35 | |
| 320 |
| Embodied Water, L/kg | 110 | |
| 440 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 | |
| 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1250 | |
| 510 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 22 |
| Strength to Weight: Axial, points | 32 | |
| 31 |
| Strength to Weight: Bending, points | 26 | |
| 25 |
| Thermal Diffusivity, mm2/s | 6.4 | |
| 3.3 |
| Thermal Shock Resistance, points | 33 | |
| 28 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0.32 to 0.42 |
| Chromium (Cr), % | 11.5 to 14 | |
| 19 to 21 |
| Cobalt (Co), % | 0 | |
| 40 to 49.8 |
| Iron (Fe), % | 77.8 to 84 | |
| 0 to 5.0 |
| Manganese (Mn), % | 0.5 to 1.0 | |
| 1.0 to 2.0 |
| Molybdenum (Mo), % | 0.5 to 1.0 | |
| 3.5 to 4.5 |
| Nickel (Ni), % | 3.5 to 5.5 | |
| 19 to 21 |
| Niobium (Nb), % | 0 | |
| 3.5 to 4.5 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tantalum (Ta), % | 0 | |
| 3.5 to 4.5 |
| Tungsten (W), % | 0 | |
| 3.5 to 4.5 |