AISI 416Se Stainless Steel vs. EN 1.6958 Steel

Both AISI 416Se stainless steel and EN 1.6958 steel are iron alloys. They have 88% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 416Se stainless steel and the bottom bar is EN 1.6958 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 230
340
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
16
Fatigue Strength, MPa 210
700
Poisson's Ratio 0.28
0.29
Reduction in Area, % 50
56
Shear Modulus, GPa 76
73
Shear Strength, MPa 340
700
Tensile Strength: Ultimate (UTS), MPa 540
1140
Tensile Strength: Yield (Proof), MPa 310
1070

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 760
450
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 30
47
Thermal Expansion, µm/m-K 10
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.9
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
9.1

Otherwise Unclassified Properties

Base Metal Price, % relative 8.0
5.0
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 1.9
2.0
Embodied Energy, MJ/kg 27
27
Embodied Water, L/kg 100
60

Common Calculations

PREN (Pitting Resistance) 13
2.9
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
180
Resilience: Unit (Modulus of Resilience), kJ/m3 250
3050
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
40
Strength to Weight: Bending, points 19
31
Thermal Diffusivity, mm2/s 8.1
13
Thermal Shock Resistance, points 20
39

Alloy Composition

Aluminum (Al), % 0
0.0050 to 0.050
Carbon (C), % 0 to 0.15
0.25 to 0.3
Chromium (Cr), % 12 to 14
1.2 to 1.7
Iron (Fe), % 83.1 to 87.9
92.6 to 94.5
Manganese (Mn), % 0 to 1.3
0.2 to 0.5
Molybdenum (Mo), % 0
0.35 to 0.55
Nickel (Ni), % 0
3.3 to 3.8
Phosphorus (P), % 0 to 0.060
0 to 0.020
Selenium (Se), % 0.15 to 0.35
0
Silicon (Si), % 0 to 1.0
0.15 to 0.3
Sulfur (S), % 0 to 0.060
0 to 0.015
Vanadium (V), % 0
0 to 0.12