AISI 416Se Stainless Steel vs. EN 1.7227 Steel

Both AISI 416Se stainless steel and EN 1.7227 steel are iron alloys. They have 87% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AISI 416Se stainless steel and the bottom bar is EN 1.7227 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 540
540 to 1850

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 760
420
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 30
46
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 8.0
2.5
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 1.9
1.5
Embodied Energy, MJ/kg 27
20
Embodied Water, L/kg 100
51

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
19 to 65
Strength to Weight: Bending, points 19
19 to 43
Thermal Diffusivity, mm2/s 8.1
12
Thermal Shock Resistance, points 20
16 to 54

Alloy Composition

Carbon (C), % 0 to 0.15
0.38 to 0.45
Chromium (Cr), % 12 to 14
0.9 to 1.2
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 83.1 to 87.9
96.5 to 98
Manganese (Mn), % 0 to 1.3
0.6 to 0.9
Molybdenum (Mo), % 0
0.15 to 0.3
Phosphorus (P), % 0 to 0.060
0 to 0.025
Selenium (Se), % 0.15 to 0.35
0
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.060
0.020 to 0.040