AISI 416Se Stainless Steel vs. S44537 Stainless Steel

Both AISI 416Se stainless steel and S44537 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 88% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 416Se stainless steel and the bottom bar is S44537 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 230
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
21
Fatigue Strength, MPa 210
230
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
79
Shear Strength, MPa 340
320
Tensile Strength: Ultimate (UTS), MPa 540
510
Tensile Strength: Yield (Proof), MPa 310
360

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Maximum Temperature: Corrosion, °C 390
530
Maximum Temperature: Mechanical, °C 760
1000
Melting Completion (Liquidus), °C 1440
1480
Melting Onset (Solidus), °C 1400
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 30
21
Thermal Expansion, µm/m-K 10
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 8.0
19
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 1.9
3.4
Embodied Energy, MJ/kg 27
50
Embodied Water, L/kg 100
140

Common Calculations

PREN (Pitting Resistance) 13
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
95
Resilience: Unit (Modulus of Resilience), kJ/m3 250
320
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
18
Strength to Weight: Bending, points 19
18
Thermal Diffusivity, mm2/s 8.1
5.6
Thermal Shock Resistance, points 20
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Carbon (C), % 0 to 0.15
0 to 0.030
Chromium (Cr), % 12 to 14
20 to 24
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 83.1 to 87.9
69 to 78.6
Lanthanum (La), % 0
0.040 to 0.2
Manganese (Mn), % 0 to 1.3
0 to 0.8
Nickel (Ni), % 0
0 to 0.5
Niobium (Nb), % 0
0.2 to 1.0
Nitrogen (N), % 0
0 to 0.040
Phosphorus (P), % 0 to 0.060
0 to 0.050
Selenium (Se), % 0.15 to 0.35
0
Silicon (Si), % 0 to 1.0
0.1 to 0.6
Sulfur (S), % 0 to 0.060
0 to 0.0060
Titanium (Ti), % 0
0.020 to 0.2
Tungsten (W), % 0
1.0 to 3.0