AISI 418 Stainless Steel vs. AWS E330H

Both AISI 418 stainless steel and AWS E330H are iron alloys. They have 62% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AISI 418 stainless steel and the bottom bar is AWS E330H.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
11
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
76
Tensile Strength: Ultimate (UTS), MPa 1100
690

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Melting Completion (Liquidus), °C 1500
1400
Melting Onset (Solidus), °C 1460
1350
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 25
12
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.8
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 3.1
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 15
30
Density, g/cm3 8.0
8.1
Embodied Carbon, kg CO2/kg material 2.9
5.4
Embodied Energy, MJ/kg 41
76
Embodied Water, L/kg 110
180

Common Calculations

PREN (Pitting Resistance) 19
17
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 38
24
Strength to Weight: Bending, points 29
22
Thermal Diffusivity, mm2/s 6.7
3.2
Thermal Shock Resistance, points 40
19

Alloy Composition

Carbon (C), % 0.15 to 0.2
0.35 to 0.45
Chromium (Cr), % 12 to 14
14 to 17
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 78.5 to 83.6
40.5 to 51.7
Manganese (Mn), % 0 to 0.5
1.0 to 2.5
Molybdenum (Mo), % 0 to 0.5
0 to 0.75
Nickel (Ni), % 1.8 to 2.2
33 to 37
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 2.5 to 3.5
0