AISI 422 Stainless Steel vs. 85-silver 15-cadmium-oxide
AISI 422 stainless steel belongs to the iron alloys classification, while 85-silver 15-cadmium-oxide belongs to the otherwise unclassified metals. There are 8 material properties with values for both materials. Properties with values for just one material (27, in this case) are not shown.
For each property being compared, the top bar is AISI 422 stainless steel and the bottom bar is 85-silver 15-cadmium-oxide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.9 | |
| 10 |
| Electrical Conductivity: Equal Volume, % IACS | 4.7 | |
| 64 to 82 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.3 | |
| 57 to 73 |
| Elongation at Break, % | 15 to 17 | |
| 2.2 to 16 |
| Shear Strength, MPa | 560 to 660 | |
| 180 to 210 |
| Strength to Weight: Axial, points | 32 to 38 | |
| 8.1 to 12 |
| Strength to Weight: Bending, points | 26 to 30 | |
| 9.7 to 13 |
| Tensile Strength: Ultimate (UTS), MPa | 910 to 1080 | |
| 290 to 440 |