AISI 422 Stainless Steel vs. EN 1.3549 Stainless Steel
Both AISI 422 stainless steel and EN 1.3549 stainless steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is AISI 422 stainless steel and the bottom bar is EN 1.3549 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 260 to 330 | |
| 220 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 910 to 1080 | |
| 730 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 280 |
| Maximum Temperature: Corrosion, °C | 380 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 650 | |
| 910 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1430 |
| Melting Onset (Solidus), °C | 1470 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 24 | |
| 21 |
| Thermal Expansion, µm/m-K | 10 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.7 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.3 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 10 |
| Density, g/cm3 | 7.9 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 3.1 | |
| 2.6 |
| Embodied Energy, MJ/kg | 44 | |
| 37 |
| Embodied Water, L/kg | 100 | |
| 130 |
Common Calculations
| PREN (Pitting Resistance) | 17 | |
| 22 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 32 to 38 | |
| 27 |
| Strength to Weight: Bending, points | 26 to 30 | |
| 24 |
| Thermal Diffusivity, mm2/s | 6.4 | |
| 5.6 |
| Thermal Shock Resistance, points | 33 to 39 | |
| 26 |
Alloy Composition
| Carbon (C), % | 0.2 to 0.25 | |
| 0.85 to 1.0 |
| Chromium (Cr), % | 11 to 12.5 | |
| 17 to 19 |
| Iron (Fe), % | 81.9 to 85.8 | |
| 77.5 to 82 |
| Manganese (Mn), % | 0.5 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.9 to 1.3 | |
| 0.9 to 1.3 |
| Nickel (Ni), % | 0.5 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.030 |
| Tungsten (W), % | 0.9 to 1.3 | |
| 0 |
| Vanadium (V), % | 0.2 to 0.3 | |
| 0.070 to 0.12 |