AISI 422 Stainless Steel vs. SAE-AISI 1017 Steel
Both AISI 422 stainless steel and SAE-AISI 1017 steel are iron alloys. They have 85% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is AISI 422 stainless steel and the bottom bar is SAE-AISI 1017 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 260 to 330 | |
| 120 to 130 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 15 to 17 | |
| 20 to 30 |
| Fatigue Strength, MPa | 410 to 500 | |
| 170 to 270 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Reduction in Area, % | 34 to 40 | |
| 46 to 56 |
| Shear Modulus, GPa | 76 | |
| 73 |
| Shear Strength, MPa | 560 to 660 | |
| 280 to 290 |
| Tensile Strength: Ultimate (UTS), MPa | 910 to 1080 | |
| 420 to 460 |
| Tensile Strength: Yield (Proof), MPa | 670 to 870 | |
| 220 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 650 | |
| 400 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1470 |
| Melting Onset (Solidus), °C | 1470 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 24 | |
| 53 |
| Thermal Expansion, µm/m-K | 10 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.7 | |
| 6.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.3 | |
| 7.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 1.8 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.1 | |
| 1.4 |
| Embodied Energy, MJ/kg | 44 | |
| 18 |
| Embodied Water, L/kg | 100 | |
| 45 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 150 | |
| 88 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1140 to 1910 | |
| 130 to 400 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 32 to 38 | |
| 15 to 16 |
| Strength to Weight: Bending, points | 26 to 30 | |
| 16 to 17 |
| Thermal Diffusivity, mm2/s | 6.4 | |
| 14 |
| Thermal Shock Resistance, points | 33 to 39 | |
| 13 to 14 |
Alloy Composition
| Carbon (C), % | 0.2 to 0.25 | |
| 0.15 to 0.2 |
| Chromium (Cr), % | 11 to 12.5 | |
| 0 |
| Iron (Fe), % | 81.9 to 85.8 | |
| 99.11 to 99.55 |
| Manganese (Mn), % | 0.5 to 1.0 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 0.9 to 1.3 | |
| 0 |
| Nickel (Ni), % | 0.5 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.050 |
| Tungsten (W), % | 0.9 to 1.3 | |
| 0 |
| Vanadium (V), % | 0.2 to 0.3 | |
| 0 |