AISI 429 Stainless Steel vs. EN 1.4835 Stainless Steel

Both AISI 429 stainless steel and EN 1.4835 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 429 stainless steel and the bottom bar is EN 1.4835 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 25
43
Fatigue Strength, MPa 180
310
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Shear Strength, MPa 300
520
Tensile Strength: Ultimate (UTS), MPa 480
750
Tensile Strength: Yield (Proof), MPa 260
350

Thermal Properties

Latent Heat of Fusion, J/g 280
320
Maximum Temperature: Corrosion, °C 400
430
Maximum Temperature: Mechanical, °C 810
1150
Melting Completion (Liquidus), °C 1440
1400
Melting Onset (Solidus), °C 1400
1360
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 26
15
Thermal Expansion, µm/m-K 10
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
17
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 2.0
3.3
Embodied Energy, MJ/kg 28
47
Embodied Water, L/kg 110
160

Common Calculations

PREN (Pitting Resistance) 15
24
Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
270
Resilience: Unit (Modulus of Resilience), kJ/m3 170
310
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
27
Strength to Weight: Bending, points 18
24
Thermal Diffusivity, mm2/s 6.9
4.0
Thermal Shock Resistance, points 17
16

Alloy Composition

Carbon (C), % 0 to 0.12
0.050 to 0.12
Cerium (Ce), % 0
0.030 to 0.080
Chromium (Cr), % 14 to 16
20 to 22
Iron (Fe), % 81.8 to 86
62 to 68.4
Manganese (Mn), % 0 to 1.0
0 to 1.0
Nickel (Ni), % 0
10 to 12
Nitrogen (N), % 0
0.12 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
1.4 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.015