AISI 429 Stainless Steel vs. C86100 Bronze

AISI 429 stainless steel belongs to the iron alloys classification, while C86100 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AISI 429 stainless steel and the bottom bar is C86100 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 25
20
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 77
43
Tensile Strength: Ultimate (UTS), MPa 480
660
Tensile Strength: Yield (Proof), MPa 260
350

Thermal Properties

Latent Heat of Fusion, J/g 280
200
Maximum Temperature: Mechanical, °C 810
170
Melting Completion (Liquidus), °C 1440
940
Melting Onset (Solidus), °C 1400
900
Specific Heat Capacity, J/kg-K 480
420
Thermal Conductivity, W/m-K 26
35
Thermal Expansion, µm/m-K 10
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
8.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
24
Density, g/cm3 7.7
8.0
Embodied Carbon, kg CO2/kg material 2.0
2.9
Embodied Energy, MJ/kg 28
49
Embodied Water, L/kg 110
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
110
Resilience: Unit (Modulus of Resilience), kJ/m3 170
530
Stiffness to Weight: Axial, points 14
7.8
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 17
23
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 6.9
10
Thermal Shock Resistance, points 17
21

Alloy Composition

Aluminum (Al), % 0
4.5 to 5.5
Carbon (C), % 0 to 0.12
0
Chromium (Cr), % 14 to 16
0
Copper (Cu), % 0
66 to 68
Iron (Fe), % 81.8 to 86
2.0 to 4.0
Lead (Pb), % 0
0 to 0.1
Manganese (Mn), % 0 to 1.0
2.5 to 5.0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 0.1
Zinc (Zn), % 0
17.3 to 25