AISI 430F Stainless Steel vs. EN 1.4435 Stainless Steel

Both AISI 430F stainless steel and EN 1.4435 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 430F stainless steel and the bottom bar is EN 1.4435 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 230
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 23
43
Fatigue Strength, MPa 210
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Shear Strength, MPa 340
420
Tensile Strength: Ultimate (UTS), MPa 540
610
Tensile Strength: Yield (Proof), MPa 310
240

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Maximum Temperature: Corrosion, °C 410
420
Maximum Temperature: Mechanical, °C 870
980
Melting Completion (Liquidus), °C 1430
1440
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
15
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.8
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 8.5
21
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.1
4.1
Embodied Energy, MJ/kg 29
57
Embodied Water, L/kg 120
160

Common Calculations

PREN (Pitting Resistance) 17
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
210
Resilience: Unit (Modulus of Resilience), kJ/m3 250
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
21
Strength to Weight: Bending, points 19
20
Thermal Diffusivity, mm2/s 6.7
4.0
Thermal Shock Resistance, points 19
14

Alloy Composition

Carbon (C), % 0 to 0.12
0 to 0.030
Chromium (Cr), % 16 to 18
17 to 19
Iron (Fe), % 79.2 to 83.9
59.8 to 68
Manganese (Mn), % 0 to 1.3
0 to 2.0
Molybdenum (Mo), % 0
2.5 to 3.0
Nickel (Ni), % 0
12.5 to 15
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.060
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0.15 to 0.35
0 to 0.015