AISI 430F Stainless Steel vs. Z13004 Zinc

AISI 430F stainless steel belongs to the iron alloys classification, while Z13004 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AISI 430F stainless steel and the bottom bar is Z13004 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
87
Elongation at Break, % 23
30
Poisson's Ratio 0.28
0.25
Shear Modulus, GPa 77
35
Tensile Strength: Ultimate (UTS), MPa 540
93
Tensile Strength: Yield (Proof), MPa 310
76

Thermal Properties

Latent Heat of Fusion, J/g 280
110
Maximum Temperature: Mechanical, °C 870
90
Melting Completion (Liquidus), °C 1430
410
Melting Onset (Solidus), °C 1390
390
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 25
110
Thermal Expansion, µm/m-K 10
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.8
27
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
37

Otherwise Unclassified Properties

Base Metal Price, % relative 8.5
11
Density, g/cm3 7.7
6.6
Embodied Carbon, kg CO2/kg material 2.1
2.8
Embodied Energy, MJ/kg 29
53
Embodied Water, L/kg 120
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
26
Resilience: Unit (Modulus of Resilience), kJ/m3 250
33
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 20
3.9
Strength to Weight: Bending, points 19
7.0
Thermal Diffusivity, mm2/s 6.7
44
Thermal Shock Resistance, points 19
2.9

Alloy Composition

Aluminum (Al), % 0
0 to 0.0020
Cadmium (Cd), % 0
0 to 0.0030
Carbon (C), % 0 to 0.12
0
Chromium (Cr), % 16 to 18
0
Copper (Cu), % 0
0 to 0.0030
Iron (Fe), % 79.2 to 83.9
0 to 0.0030
Lead (Pb), % 0
0 to 0.0030
Manganese (Mn), % 0 to 1.3
0
Phosphorus (P), % 0 to 0.060
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0.15 to 0.35
0
Tin (Sn), % 0
0 to 0.0010
Zinc (Zn), % 0
99.985 to 100