AISI 431 Stainless Steel vs. R60802 Alloy

AISI 431 stainless steel belongs to the iron alloys classification, while R60802 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AISI 431 stainless steel and the bottom bar is R60802 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
98
Elongation at Break, % 15 to 17
22
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 77
36
Tensile Strength: Ultimate (UTS), MPa 890 to 1380
430
Tensile Strength: Yield (Proof), MPa 710 to 1040
270

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Specific Heat Capacity, J/kg-K 480
270
Thermal Conductivity, W/m-K 26
22
Thermal Expansion, µm/m-K 12
6.0

Otherwise Unclassified Properties

Density, g/cm3 7.7
6.5
Embodied Water, L/kg 120
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 180
85
Resilience: Unit (Modulus of Resilience), kJ/m3 1270 to 2770
380
Stiffness to Weight: Axial, points 14
8.3
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 32 to 50
18
Strength to Weight: Bending, points 27 to 36
19
Thermal Diffusivity, mm2/s 7.0
12
Thermal Shock Resistance, points 28 to 43
53

Alloy Composition

Carbon (C), % 0 to 0.2
0
Chromium (Cr), % 15 to 17
0.050 to 0.15
Iron (Fe), % 78.2 to 83.8
0.070 to 0.2
Manganese (Mn), % 0 to 1.0
0
Nickel (Ni), % 1.3 to 2.5
0.030 to 0.080
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
1.2 to 1.7
Zirconium (Zr), % 0
97.8 to 98.7
Residuals, % 0
0 to 0.11