AISI 436 Stainless Steel vs. EN 1.0452 Steel

Both AISI 436 stainless steel and EN 1.0452 steel are iron alloys. They have 81% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 436 stainless steel and the bottom bar is EN 1.0452 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
120
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
25
Fatigue Strength, MPa 190
210
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 320
270
Tensile Strength: Ultimate (UTS), MPa 500
430
Tensile Strength: Yield (Proof), MPa 270
290

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 880
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
48
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.1
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.7
1.5
Embodied Energy, MJ/kg 38
19
Embodied Water, L/kg 120
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
94
Resilience: Unit (Modulus of Resilience), kJ/m3 190
220
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
15
Strength to Weight: Bending, points 18
16
Thermal Diffusivity, mm2/s 6.7
13
Thermal Shock Resistance, points 18
13

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Carbon (C), % 0 to 0.12
0 to 0.17
Chromium (Cr), % 16 to 18
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 77.8 to 83.3
97.1 to 99.58
Manganese (Mn), % 0 to 1.0
0.4 to 1.2
Molybdenum (Mo), % 0.75 to 1.3
0 to 0.080
Nickel (Ni), % 0
0 to 0.3
Niobium (Nb), % 0 to 0.8
0 to 0.010
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 0.040
Vanadium (V), % 0
0 to 0.020