AISI 440A Stainless Steel vs. Austenitic Nodular Cast Iron
Both AISI 440A stainless steel and austenitic nodular cast iron are iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is AISI 440A stainless steel and the bottom bar is austenitic nodular cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 180 to 190 |
| Elongation at Break, % | 5.0 to 20 | |
| 6.8 to 34 |
| Poisson's Ratio | 0.28 | |
| 0.29 to 0.3 |
| Shear Modulus, GPa | 77 | |
| 70 to 72 |
| Tensile Strength: Ultimate (UTS), MPa | 730 to 1790 | |
| 430 to 500 |
| Tensile Strength: Yield (Proof), MPa | 420 to 1650 | |
| 190 to 240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 280 to 350 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1340 to 1400 |
| Melting Onset (Solidus), °C | 1370 | |
| 1300 to 1360 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 to 490 |
| Thermal Expansion, µm/m-K | 10 | |
| 13 to 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.0 | |
| 16 to 25 |
| Density, g/cm3 | 7.7 | |
| 7.7 to 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.2 | |
| 3.5 to 4.9 |
| Embodied Energy, MJ/kg | 31 | |
| 48 to 68 |
| Embodied Water, L/kg | 120 | |
| 91 to 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 87 to 120 | |
| 24 to 140 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 to 25 |
| Strength to Weight: Axial, points | 26 to 65 | |
| 15 to 18 |
| Strength to Weight: Bending, points | 23 to 43 | |
| 16 to 18 |
| Thermal Shock Resistance, points | 26 to 65 | |
| 12 to 15 |