AISI 440A Stainless Steel vs. EN 1.4477 Stainless Steel
Both AISI 440A stainless steel and EN 1.4477 stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is AISI 440A stainless steel and the bottom bar is EN 1.4477 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Elongation at Break, % | 5.0 to 20 | |
| 22 to 23 |
| Fatigue Strength, MPa | 270 to 790 | |
| 420 to 490 |
| Poisson's Ratio | 0.28 | |
| 0.27 |
| Shear Modulus, GPa | 77 | |
| 81 |
| Shear Strength, MPa | 450 to 1040 | |
| 550 to 580 |
| Tensile Strength: Ultimate (UTS), MPa | 730 to 1790 | |
| 880 to 930 |
| Tensile Strength: Yield (Proof), MPa | 420 to 1650 | |
| 620 to 730 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 300 |
| Maximum Temperature: Corrosion, °C | 400 | |
| 460 |
| Maximum Temperature: Mechanical, °C | 760 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1430 |
| Melting Onset (Solidus), °C | 1370 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 23 | |
| 13 |
| Thermal Expansion, µm/m-K | 10 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.5 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.9 | |
| 2.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.0 | |
| 20 |
| Density, g/cm3 | 7.7 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 2.2 | |
| 3.7 |
| Embodied Energy, MJ/kg | 31 | |
| 52 |
| Embodied Water, L/kg | 120 | |
| 190 |
Common Calculations
| PREN (Pitting Resistance) | 18 | |
| 41 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 87 to 120 | |
| 180 to 190 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 26 to 65 | |
| 31 to 33 |
| Strength to Weight: Bending, points | 23 to 43 | |
| 26 to 27 |
| Thermal Diffusivity, mm2/s | 6.2 | |
| 3.5 |
| Thermal Shock Resistance, points | 26 to 65 | |
| 23 to 25 |
Alloy Composition
| Carbon (C), % | 0.6 to 0.75 | |
| 0 to 0.030 |
| Chromium (Cr), % | 16 to 18 | |
| 28 to 30 |
| Copper (Cu), % | 0 | |
| 0 to 0.8 |
| Iron (Fe), % | 78.4 to 83.4 | |
| 56.6 to 63.6 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.8 to 1.5 |
| Molybdenum (Mo), % | 0 to 0.75 | |
| 1.5 to 2.6 |
| Nickel (Ni), % | 0 | |
| 5.8 to 7.5 |
| Nitrogen (N), % | 0 | |
| 0.3 to 0.4 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.015 |