AISI 440C Stainless Steel vs. 92-silver 8-tin-oxide
AISI 440C stainless steel belongs to the iron alloys classification, while 92-silver 8-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is AISI 440C stainless steel and the bottom bar is 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 76 to 80 |
| Elongation at Break, % | 2.0 to 14 | |
| 32 to 34 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 39 to 88 | |
| 62 to 110 |
| Shear Strength, MPa | 430 to 1120 | |
| 150 to 210 |
| Tensile Strength: Ultimate (UTS), MPa | 710 to 1970 | |
| 230 to 320 |
| Tensile Strength: Yield (Proof), MPa | 450 to 1900 | |
| 120 to 300 |