AISI 440C Stainless Steel vs. SAE-AISI M30 Steel

Both AISI 440C stainless steel and SAE-AISI M30 steel are iron alloys. They have 84% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AISI 440C stainless steel and the bottom bar is SAE-AISI M30 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
78
Tensile Strength: Ultimate (UTS), MPa 710 to 1970
800 to 2170

Thermal Properties

Latent Heat of Fusion, J/g 280
270
Melting Completion (Liquidus), °C 1480
1550
Melting Onset (Solidus), °C 1370
1500
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 22
24
Thermal Expansion, µm/m-K 10
12

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
26
Density, g/cm3 7.7
8.2
Embodied Carbon, kg CO2/kg material 2.2
7.2
Embodied Energy, MJ/kg 31
100
Embodied Water, L/kg 120
120

Common Calculations

PREN (Pitting Resistance) 18
35
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 26 to 71
27 to 74
Strength to Weight: Bending, points 23 to 46
24 to 46
Thermal Diffusivity, mm2/s 6.0
6.6
Thermal Shock Resistance, points 26 to 71
25 to 67

Alloy Composition

Carbon (C), % 1.0 to 1.2
0.75 to 0.85
Chromium (Cr), % 16 to 18
3.5 to 4.3
Cobalt (Co), % 0
4.5 to 5.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 78 to 83.1
75.2 to 80.9
Manganese (Mn), % 0 to 1.0
0.15 to 0.4
Molybdenum (Mo), % 0 to 0.75
7.8 to 9.0
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0.2 to 0.45
Sulfur (S), % 0 to 0.015
0 to 0.030
Tungsten (W), % 0
1.3 to 2.3
Vanadium (V), % 0
1.0 to 1.4

Comparable Variants