AISI 440C Stainless Steel vs. N06035 Nickel
AISI 440C stainless steel belongs to the iron alloys classification, while N06035 nickel belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is AISI 440C stainless steel and the bottom bar is N06035 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Elongation at Break, % | 2.0 to 14 | |
| 34 |
| Fatigue Strength, MPa | 260 to 840 | |
| 200 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 84 |
| Shear Strength, MPa | 430 to 1120 | |
| 440 |
| Tensile Strength: Ultimate (UTS), MPa | 710 to 1970 | |
| 660 |
| Tensile Strength: Yield (Proof), MPa | 450 to 1900 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 340 |
| Maximum Temperature: Mechanical, °C | 870 | |
| 1030 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1440 |
| Melting Onset (Solidus), °C | 1370 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 450 |
| Thermal Expansion, µm/m-K | 10 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.0 | |
| 60 |
| Density, g/cm3 | 7.7 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 2.2 | |
| 10 |
| Embodied Energy, MJ/kg | 31 | |
| 140 |
| Embodied Water, L/kg | 120 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 39 to 88 | |
| 180 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 26 to 71 | |
| 22 |
| Strength to Weight: Bending, points | 23 to 46 | |
| 20 |
| Thermal Shock Resistance, points | 26 to 71 | |
| 17 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.4 |
| Carbon (C), % | 1.0 to 1.2 | |
| 0 to 0.050 |
| Chromium (Cr), % | 16 to 18 | |
| 32.3 to 34.3 |
| Cobalt (Co), % | 0 | |
| 0 to 1.0 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 78 to 83.1 | |
| 0 to 2.0 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 to 0.75 | |
| 7.6 to 9.0 |
| Nickel (Ni), % | 0 | |
| 51.1 to 60.2 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.015 |
| Tungsten (W), % | 0 | |
| 0 to 0.6 |
| Vanadium (V), % | 0 | |
| 0 to 0.2 |