AISI 445 Stainless Steel vs. AWS E80C-B6

Both AISI 445 stainless steel and AWS E80C-B6 are iron alloys. They have 84% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AISI 445 stainless steel and the bottom bar is AWS E80C-B6.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
19
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
74
Tensile Strength: Ultimate (UTS), MPa 480
630
Tensile Strength: Yield (Proof), MPa 230
530

Thermal Properties

Latent Heat of Fusion, J/g 290
260
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 21
39
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.6
8.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
9.5

Otherwise Unclassified Properties

Base Metal Price, % relative 12
4.7
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.6
1.8
Embodied Energy, MJ/kg 38
25
Embodied Water, L/kg 130
71

Common Calculations

PREN (Pitting Resistance) 20
7.1
Resilience: Ultimate (Unit Rupture Work), MJ/m3 98
120
Resilience: Unit (Modulus of Resilience), kJ/m3 140
730
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
22
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 5.6
11
Thermal Shock Resistance, points 16
18

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.1
Chromium (Cr), % 19 to 21
4.5 to 6.0
Copper (Cu), % 0.3 to 0.6
0 to 0.35
Iron (Fe), % 74.9 to 80.7
90.1 to 94.4
Manganese (Mn), % 0 to 1.0
0.4 to 1.0
Molybdenum (Mo), % 0
0.45 to 0.65
Nickel (Ni), % 0 to 0.6
0 to 0.6
Niobium (Nb), % 0 to 0.8
0
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0.25 to 0.6
Sulfur (S), % 0 to 0.012
0 to 0.025
Vanadium (V), % 0
0 to 0.030
Residuals, % 0
0 to 0.5