AISI 446 Stainless Steel vs. EN 1.8864 Steel

Both AISI 446 stainless steel and EN 1.8864 steel are iron alloys. They have 75% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AISI 446 stainless steel and the bottom bar is EN 1.8864 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 23
22
Fatigue Strength, MPa 200
320
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
73
Shear Strength, MPa 360
380
Tensile Strength: Ultimate (UTS), MPa 570
610
Tensile Strength: Yield (Proof), MPa 300
460

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 1180
410
Melting Completion (Liquidus), °C 1510
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 17
39
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.8
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.4
1.7
Embodied Energy, MJ/kg 35
22
Embodied Water, L/kg 150
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
120
Resilience: Unit (Modulus of Resilience), kJ/m3 230
550
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 26
24
Strength to Weight: Axial, points 21
22
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 4.6
10
Thermal Shock Resistance, points 19
18

Alloy Composition

Boron (B), % 0
0 to 0.0050
Carbon (C), % 0 to 0.2
0 to 0.18
Chromium (Cr), % 23 to 27
0 to 0.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 69.2 to 77
95.1 to 100
Manganese (Mn), % 0 to 1.5
0 to 1.7
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0 to 0.75
0 to 1.0
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0 to 0.25
0 to 0.015
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.0050
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.080
Zirconium (Zr), % 0
0 to 0.050