AISI W2 Steel vs. EN 1.3558 Steel
Both AISI W2 steel and EN 1.3558 steel are iron alloys. They have 77% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is AISI W2 steel and the bottom bar is EN 1.3558 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 2400 | |
| 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 240 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1810 |
| Melting Onset (Solidus), °C | 1410 | |
| 1760 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 410 |
| Thermal Conductivity, W/m-K | 45 | |
| 20 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.3 | |
| 45 |
| Density, g/cm3 | 7.8 | |
| 9.3 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 8.4 |
| Embodied Energy, MJ/kg | 29 | |
| 130 |
| Embodied Water, L/kg | 48 | |
| 90 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 12 |
| Stiffness to Weight: Bending, points | 24 | |
| 21 |
| Strength to Weight: Axial, points | 21 to 86 | |
| 23 |
| Strength to Weight: Bending, points | 20 to 51 | |
| 20 |
| Thermal Diffusivity, mm2/s | 12 | |
| 5.3 |
| Thermal Shock Resistance, points | 19 to 80 | |
| 22 |
Alloy Composition
| Carbon (C), % | 0.85 to 1.5 | |
| 0.7 to 0.8 |
| Chromium (Cr), % | 0 to 0.15 | |
| 3.9 to 4.3 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.3 |
| Iron (Fe), % | 96.2 to 98.6 | |
| 73.7 to 77.6 |
| Manganese (Mn), % | 0.35 to 0.74 | |
| 0 to 0.4 |
| Molybdenum (Mo), % | 0 to 0.1 | |
| 0 to 0.6 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.1 to 0.4 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.015 |
| Tungsten (W), % | 0 to 0.15 | |
| 17.5 to 19 |
| Vanadium (V), % | 0.15 to 0.35 | |
| 1.0 to 1.3 |