AISI W2 Steel vs. SAE-AISI P6 Steel
Both AISI W2 steel and SAE-AISI P6 steel are iron alloys. They have a very high 95% of their average alloy composition in common.
For each property being compared, the top bar is AISI W2 steel and the bottom bar is SAE-AISI P6 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 2400 | |
| 630 to 1930 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 45 | |
| 43 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 7.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 9.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.3 | |
| 4.6 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 1.8 |
| Embodied Energy, MJ/kg | 29 | |
| 24 |
| Embodied Water, L/kg | 48 | |
| 59 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 21 to 86 | |
| 22 to 68 |
| Strength to Weight: Bending, points | 20 to 51 | |
| 21 to 44 |
| Thermal Diffusivity, mm2/s | 12 | |
| 11 |
| Thermal Shock Resistance, points | 19 to 80 | |
| 21 to 63 |
Alloy Composition
| Carbon (C), % | 0.85 to 1.5 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 0 to 0.15 | |
| 1.3 to 1.8 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.25 |
| Iron (Fe), % | 96.2 to 98.6 | |
| 92.9 to 95 |
| Manganese (Mn), % | 0.35 to 0.74 | |
| 0.35 to 0.7 |
| Molybdenum (Mo), % | 0 to 0.1 | |
| 0 |
| Nickel (Ni), % | 0 to 0.2 | |
| 3.3 to 3.8 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.1 to 0.4 | |
| 0.1 to 0.4 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 to 0.15 | |
| 0 |
| Vanadium (V), % | 0.15 to 0.35 | |
| 0 |