AISI W2 Steel vs. N06045 Nickel
AISI W2 steel belongs to the iron alloys classification, while N06045 nickel belongs to the nickel alloys. They have a modest 24% of their average alloy composition in common, which, by itself, doesn't mean much. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is AISI W2 steel and the bottom bar is N06045 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 72 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 2400 | |
| 690 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 350 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1350 |
| Melting Onset (Solidus), °C | 1410 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.3 | |
| 42 |
| Density, g/cm3 | 7.8 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 6.9 |
| Embodied Energy, MJ/kg | 29 | |
| 98 |
| Embodied Water, L/kg | 48 | |
| 250 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 21 to 86 | |
| 24 |
| Strength to Weight: Bending, points | 20 to 51 | |
| 22 |
| Thermal Shock Resistance, points | 19 to 80 | |
| 18 |
Alloy Composition
| Carbon (C), % | 0.85 to 1.5 | |
| 0.050 to 0.12 |
| Cerium (Ce), % | 0 | |
| 0.030 to 0.090 |
| Chromium (Cr), % | 0 to 0.15 | |
| 26 to 29 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.3 |
| Iron (Fe), % | 96.2 to 98.6 | |
| 21 to 25 |
| Manganese (Mn), % | 0.35 to 0.74 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 to 0.1 | |
| 0 |
| Nickel (Ni), % | 0 to 0.2 | |
| 45 to 50.4 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.020 |
| Silicon (Si), % | 0.1 to 0.4 | |
| 2.5 to 3.0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 to 0.15 | |
| 0 |
| Vanadium (V), % | 0.15 to 0.35 | |
| 0 |