AM60B Magnesium vs. 5454 Aluminum
AM60B magnesium belongs to the magnesium alloys classification, while 5454 aluminum belongs to the aluminum alloys.
For each property being compared, the top bar is AM60B magnesium and the bottom bar is 5454 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 62 | |
| 61 to 93 |
| Elastic (Young's, Tensile) Modulus, GPa | 45 | |
| 69 |
| Elongation at Break, % | 11 | |
| 2.3 to 18 |
| Fatigue Strength, MPa | 96 | |
| 83 to 160 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 17 | |
| 26 |
| Shear Strength, MPa | 140 | |
| 140 to 200 |
| Tensile Strength: Ultimate (UTS), MPa | 230 | |
| 230 to 350 |
| Tensile Strength: Yield (Proof), MPa | 130 | |
| 97 to 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 190 |
| Melting Completion (Liquidus), °C | 620 | |
| 650 |
| Melting Onset (Solidus), °C | 540 | |
| 600 |
| Specific Heat Capacity, J/kg-K | 1000 | |
| 900 |
| Thermal Conductivity, W/m-K | 61 | |
| 130 |
| Thermal Expansion, µm/m-K | 26 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 13 | |
| 34 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 72 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 9.5 |
| Density, g/cm3 | 1.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 8.6 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 990 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 | |
| 6.3 to 34 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 | |
| 68 to 590 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 71 | |
| 50 |
| Strength to Weight: Axial, points | 38 | |
| 23 to 36 |
| Strength to Weight: Bending, points | 50 | |
| 30 to 41 |
| Thermal Diffusivity, mm2/s | 37 | |
| 55 |
| Thermal Shock Resistance, points | 14 | |
| 10 to 16 |
Alloy Composition
| Aluminum (Al), % | 5.5 to 6.5 | |
| 94.5 to 97.1 |
| Chromium (Cr), % | 0 | |
| 0.050 to 0.2 |
| Copper (Cu), % | 0 to 0.010 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.0050 | |
| 0 to 0.4 |
| Magnesium (Mg), % | 92.6 to 94.3 | |
| 2.4 to 3.0 |
| Manganese (Mn), % | 0.24 to 0.6 | |
| 0.5 to 1.0 |
| Nickel (Ni), % | 0 to 0.0020 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.25 |
| Titanium (Ti), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 to 0.22 | |
| 0 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |