ASTM A148 Cast Steel vs. C55283 Copper
ASTM A148 cast steel belongs to the iron alloys classification, while C55283 copper belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is ASTM A148 cast steel and the bottom bar is C55283 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 100 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 630 to 1300 | |
| 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 400 to 430 | |
| 200 |
| Melting Completion (Liquidus), °C | 1460 | |
| 720 |
| Melting Onset (Solidus), °C | 1420 | |
| 640 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 400 |
| Thermal Expansion, µm/m-K | 13 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 1.7 | |
| 7.9 |
| Embodied Energy, MJ/kg | 20 to 22 | |
| 120 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 22 to 46 | |
| 6.1 |
| Strength to Weight: Bending, points | 21 to 34 | |
| 8.5 |
| Thermal Shock Resistance, points | 18 to 38 | |
| 8.0 |