ASTM A182 Grade F10 vs. ACI-ASTM CT15C Steel
Both ASTM A182 grade F10 and ACI-ASTM CT15C steel are iron alloys. They have 75% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is ASTM A182 grade F10 and the bottom bar is ACI-ASTM CT15C steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 | |
| 140 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 34 | |
| 23 |
| Fatigue Strength, MPa | 180 | |
| 130 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 74 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 630 | |
| 500 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 600 | |
| 1080 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1410 |
| Melting Onset (Solidus), °C | 1370 | |
| 1360 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Expansion, µm/m-K | 13 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 15 | |
| 1.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 17 | |
| 1.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 18 | |
| 36 |
| Density, g/cm3 | 7.9 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 6.1 |
| Embodied Energy, MJ/kg | 51 | |
| 88 |
| Embodied Water, L/kg | 120 | |
| 190 |
Common Calculations
| PREN (Pitting Resistance) | 8.0 | |
| 20 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
| 90 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 | |
| 93 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 22 | |
| 17 |
| Strength to Weight: Bending, points | 21 | |
| 17 |
| Thermal Shock Resistance, points | 18 | |
| 12 |
Alloy Composition
| Carbon (C), % | 0.1 to 0.2 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 7.0 to 9.0 | |
| 19 to 21 |
| Iron (Fe), % | 66.5 to 72.4 | |
| 40.3 to 49.2 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0.15 to 1.5 |
| Nickel (Ni), % | 19 to 22 | |
| 31 to 34 |
| Niobium (Nb), % | 0 | |
| 0.5 to 1.5 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.030 |
| Silicon (Si), % | 1.0 to 1.4 | |
| 0.15 to 1.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |